310S Stainless Steel Plate
Stainless steel 310S is an austenitic heat resistant alloy with excellent resistance to oxidation under mildly cyclic conditions through 2000 F degree. Its high chromium and nickel contents provide comparable corrosion resistance, superior resistance to oxidation and the retention of a larger fraction of room temperature strength than the common austenitic alloys like Type 304. Stainless 310 is often used at cryogenic temperatures, with excellent toughness to -450 F degree, and low magnetic permeability. Stainless Steel 1.4845 (310S) is used when the application environment involves moist corrodents in a temperature range lower than that which is normally considered "high temperature" service. The lower carbon content of SS 310S does reduce its high temperature strength compared to 310.
Chemical composition: % Cr 24.0-26.0 Ni 19.0-22.0 C 0.08 Max Si 1.50 Max Mn 2.00 Max P 0.045 Max S 0.03 Max Mo 0.75 Max Cu 0.50 Max Fe Balance
Mechanical Properties: Tensile Strength Psi 75000 , MPa 515 Yield Strength (0.2%Offset) Psi 30000 , MPa 205 Elongation 35 % Sheet Size: Thickness 0.6-30mm Width 1000-1500mm Length 2000-6000mm
Specifications AMS 5521, AMS 5651 ASME SA 240, ASME SA 312, ASME SA 479 ASTM A 240, ASTM A 276, ASTM A 276 Condition A, ASTM A 276 Condition S, ASTM A 312, ASTM A 479 EN 10095 UNS S31008, UNS S31009 Werkstoff 1.4845
Fabrication with Stainless 310/310S Type 310/310S is readily fabricated by standard commercial procedures. In comparison to carbon steel, stainless steels are tougher and tend to work harden rapidly. Type 310/310S can be welded using all of the common welding processes.
Applications:
|